Kimya ABS Carbon Fibre 3D Printing filament 2.85mm 500gms

Name: Kimya ABS Carbon Fibre 3D Printing filament 2.85mm 500gms
Brand: Kimya
SKU: kim-absCF-285-500
Price: 60.48 GBP
Availability: InStock

Kimya ABS Carbon Fibre 3D Printing filament 2.85mm 500gms

£50.40 £60.48 (inc. VAT)

Stock Status: In Stock

ABS Carbon Fibre by Kimya is a mixture of high quality ABS resin and carbon fibers. The carbon fibers give the filament improved rigidity compared to a standard ABS. Great for high strength modelling, RC drone creation and tool making.

You Will Earn 60 points with this purchase

Make 6 weekly payments of £10.08.

Interest free. Learn More

Information Specifications Reviews

The Kimya ABS Carbon 3D filament belongs to the styrenic polymer family. Acrylonitrile-butadiene-styrene-carbon (ABS Carbon) is a mixture of ABS and carbon fibre's. The carbon fibre's give the filament improved rigidity compared to a standard ABS. This filament is highly valued by manufacturers of drones and by modelling aficionados. It is also used to make tools. The Kimya ABS Carbon 3D filament has the following properties:

No shrinkage
Better tensile modulus than ABS-S
Less warpage than ABS-S
Complies with the REACH standard

2-year ARMOR warranty.

FILAMENT PROPERTIES

PROPERTIES	TEST METHODS	VALUES
Diameter	INS-6712	1.75 ± 0.1 mm 2.85 ± 0.1 mm
Density	ISO 1183-1	1.045 g/cm3
Moisture rate	INS-6711	< 1 %
Melt flow index (MFI)	ISO 1133-1 (@220°C – 10 kg)	17.4 g/10min
Glass transition temperature (Tg)	ISO 11357-1 DSC (10°C/min - 20-220°C)	100 °C
Melting Temperature (Tm)	ISO 11357-1 DSC (10°C/min – 20-220°C)	30 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION	XY
Printing Speed	50-60 mm/s
Infill	100% - rectilinear
Infill Angle	45°/-45°
Nozzle Temperature	245-270°C
Bed T°	90-95°C

PRINTED SPECIMENS PROPERTIES

	PROPERTIES	TEST METHODS	VALUES
MECHANICAL PROPERTIES	Tensile modulus	ISO 527-2/5A/50	2,665 MPa
	Tensile Strength	ISO 527-2/5A/50	35.7 MPa
	Tensile Stress at Break	ISO 527-2/5A/50	37.5 MPa
	Tensile strain at break	ISO 527	2 %
	Flexural modulus	ISO 178	1,809 MPa
	Flexural stress at conventional deflection (3,5% strain)*	ISO 178	51.4 MPa
	Charpy impact resistance	ISO 179-1/1eA	6.2 kJ/m²
	Shore Hardness	ISO 868	72.7

Note 1

*According to ISO 178, end of the test at 5% deformation even if there is no specimen break.

Note 2

The data should be considered as indicative values - Properties can be influenced by production conditions.

PRINT SETTINGS:

PRINT SPEED : 40-70 mm/s
EXTRUSION TEMPERATURE : 250-270°C
PLATFORM TEMPERATURE : 90-110°C

For more information on the Armor Kimya ABS Carbon & Kevlar 3D printing filaments view here.

Filament Brand:

Kimya

Filament Type:

ABS Carbon Fibre

Filament Diameter:

2.85mm

Filament Colour:

Black

Filament Weight:

500gms

Brand:

Kimya