Kimya PEKK Carbon 3D filament belongs to the polyaryletherketone family. Polyetherketoneketone (PEKK) is a thermoplastic polymer reinforced with carbon fiber. Compared to PEEK, PEKK Carbon offers slower crystallisation speed enabling transformation at lower room temperatures. It enables parts to be created with improved visual finish and better mechanical properties.
You Will Earn 464 points with this purchase

Make 6 weekly payments of £77.40.

Interest free. Learn More

The Kimya PEKK Carbon 3D filament belongs to the polyaryletherketone family. Polyetherketoneketone (PEKK) is a thermoplastic polymer reinforced with carbon fibre. This combination gives it a high level of rigidity and heat-resistance. It can be used as a material in components exposed to acids and hydrocarbons, such as fuel and lubricants, and also to produce components located in engine housings. The Kimya PEKK Carbon 3D filament has the following properties:

  • Temperature resistance
  • Reinforced with carbon fibre
  • Complies with the REACH standard

2-year ARMOR warranty.

(PEKK) is a material derived from semi-cristalline thermoplastics, the polyaryletherketones (PAEKs). It is a family of materials that offers excellent thermomechanical properties and also includes PEEK, the material from the family currently most widely used.

PAEK is composed of ether and ketone; their ratio and functions influence the polymers’ glass transition and fusion temperature, thereby affecting their thermal resistance and blocking temperature. It is a material that offers numerous advantages such as its high level of rigidity; it is frequently compared to aluminium, although it is 40% lighter. It also offers a high level of resistance to UV and high temperatures, in addition to good chemical and abrasion resistance. However, it is expensive and difficult to transform. Additionally, few 3D printers are able to use the filament, further restricting its possibilities. Its rough surface and limited colours (black, blue, beige and green) are also drawbacks for PAEK.

FILAMENT PROPERTIES

PROPERTIES TEST METHODS VALUES
Diameter INS-6712 1.75 ± 0.1 mm
2.85 ± 0.1 mm
Density ISO 1183-1 1.27 g/cm3
Moisture rate INS-6711 < 1 %
Glass transition temperature (Tg) ISO 11357-1 DSC (10°C/min - 20-410°C) 160 °C

PRINT PARAMETERS AND SPECIMENS DIMENSIONS

PRINTING DIRECTION XY
Printing Speed 20-40 mm/s
Infill 100% - rectilinear
Infill Angle 45°/-45°
Nozzle Temperature 350-390°C
Bed T° 110-150°C

PRINTED SPECIMENS PROPERTIES

PROPERTIES TEST METHODS VALUES
THERMAL PROPERTIES Maximum use T° - 150 °C
ELECTRICAL PROPERTIES Dielectric strength IEC 60243-1 (100µm) 84 KV/mm
Surface resistivity ASTM D257 1016 Ohms/m²
MECHANICAL PROPERTIES Tensile modulus ISO 527 2,900 MPa
Tensile Strength ISO 527 39.1 MPa
Tensile strain at break ISO 527 3 %
Flexural modulus ISO 178 2,924 MPa
Flexural strength* ISO 178 85.9 %
Charpy impact resistance ISO 179-1/1eA 5 kJ/m²

Note 1

*According to ISO 178, end of the test at 5% deformation even if there is no specimen break.
Note 2 The data should be considered as indicative values - Properties can be influenced by production conditions.

PRINT SETTINGS:

  • PRINT SPEED : 20-40 mm/s
  • EXTRUSION TEMPERATURE : 350-390°C
  • PLATFORM TEMPERATURE : 110-150°C

MISCELLANEOUS

Spool Material PC
Steaming Temperature 120°C
Steaming Duration 4h-6h

Find more information about our Kimya PEKK Carbon 3D filament:

  

  • Filament Brand:
    Kimya
  • Filament Type:
    PEKK Carbon
  • Filament Diameter:
    2.85mm
  • Filament Colour:
    Black
  • Brand:
    Kimya
  • Condition:
    New
  • Product Code:
    kim-PEKKCAR-285-500
  • Weight:
    0.5kg
product review overlay image

Customer reviews

No reviews left yet
Write a review

No reviews have been left for this product, be the first to leave a review